Designation: A1010/A1010M −24
Standard Speciﬁcation for
Higher-Strength Martensitic Stainless Steel Plate, Sheet, and
Strip
1
This standard is issued under the ﬁxed designation A1010/A1010M; the number immediately following the designation indicates the
year of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last
reapproval. A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope*
1.1 This speciﬁcation covers martensitic stainless steels for
various structural, architectural, pressure vessel, and heat-
resisting applications. The mechanical properties of these
steels are customarily, but not necessarily, developed by a
suitable heat treatment generally referred to as tempering.
1.2 Steel products under this speciﬁcation are available in
two grades:
Grade Yield Strength, min, ksi [MPa]
40 [275] 40 [275]
50 [345] 50 [345]
1.3 The maximum thickness of plates is limited only by the
capacity of the composition to meet the speciﬁed mechanical
property requirements; however, current practice normally
limits the maximum thickness of plates furnished under this
speciﬁcation to 2 in. [50 mm].
1.4 This speciﬁcation is expressed in both inch-pound units
and in SI units; however, unless the purchase order or contract
speciﬁes the applicable Mspeciﬁcation designation (SI units),
the inch-pound units shall apply. The values stated in either SI
units or inch-pound units are to be regarded separately as
standard. Within the text, the SI units are shown in brackets.
The values stated in each system may not be exact equivalents;
therefore, each system shall be used independently of the other.
Combining values from the two systems may result in non-
conformance with the standard.
1.5 Supplementary requirements are provided for use at the
option of the purchaser. The supplementary requirements shall
apply only when speciﬁed individually by the purchaser in the
purchase order or contract.
1.6 This standard does not purport to address all of the
safety concerns, if any, associated with its use. It is the
responsibility of the user of this standard to establish appro-
priate safety, health, and environmental practices and deter-
mine the applicability of regulatory limitations prior to use.
1.7 This international standard was developed in accor-
dance with internationally recognized principles on standard-
ization established in the Decision on Principles for the
Development of International Standards, Guides and Recom-
mendations issued by the World Trade Organization Technical
Barriers to Trade (TBT) Committee.
2. Referenced Documents
2.1 ASTM Standards:
2
A480/A480M Speciﬁcation for General Requirements for
Flat-Rolled Stainless and Heat-Resisting Steel Plate,
Sheet, and Strip
A673/A673M Speciﬁcation for Sampling Procedure for Im-
pact Testing of Structural Steel
A941 Terminology Relating to Steel, Stainless Steel, Related
Alloys, and Ferroalloys
E527 Practice for Numbering Metals and Alloys in the
Uniﬁed Numbering System (UNS)
2.2 Other Document:
SAE J1086 Recommended Practice for Numbering Metals
and Alloys
3
3. Terminology
3.1 Deﬁnitions:
3.1.1 For deﬁnitions of terms used in this standard, refer to
Terminology A941.
3.1.2 For deﬁnitions of terms pertaining to plate, sheet, and
strip, refer to Speciﬁcation A480/A480M.
4. General Requirements
4.1 The following requirements for orders for material
furnished under this speciﬁcation shall conform to the appli-
cable requirements of the current edition of Speciﬁcation
A480/A480M.
4.1.1 Ordering Information,
4.1.2 Process,
1
This speciﬁcation is under the jurisdiction of ASTM Committee A01 on Steel,
Stainless Steel and Related Alloys and is the direct responsibility of Subcommittee
A01.17 on Flat-Rolled and Wrought Stainless Steel.
Current edition approved March 1, 2024. Published March 2024. Originally
approved in 2000. Last previous edition approved in 2018 as A1010/A1010M – 13
(2018). DOI: 10.1520/A1010_A1010M-24.
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
Standards volume information, refer to the standard’s Document Summary page on
the ASTM website.
3
Available from Society of Automotive Engineers (SAE), 400 Commonwealth
Dr., Warrendale, PA 15096-0001, http://www.sae.org.
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the
Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
1

4.1.3 Heat Analysis,

4.1.4 Product Analysis,

4.1.5 Finish for Sheet,

4.1.6 Finish for Strip,

4.1.7 Finish for Plates,

4.1.8 Test Specimens,

4.1.9 Number of Tests,

4.1.10 Test Methods,

4.1.11 Retests and Retreatment,

4.1.12 Dimensions and Permissible Variations,

4.1.13 Workmanship,

4.1.14 Packaging, Marking, and Loading,

4.1.15 Inspection,

4.1.16 Rejection and Rehearing, and

4.1.17 Material Test Report and Certiﬁcation.

5. Chemical Composition

5.1 The steel shall conform to the requirements as to

chemical composition speciﬁed in Table 1, and shall conform

to applicable requirements speciﬁed in the current edition of

Speciﬁcation A480/A480M.

TABLE 1 Chemical Composition Requirements, %

UNS

Designation

Type Carbon Manganese Phosphorus Sulfur Silicon Chromium Nickel Molybdenum Nitrogen Other

Elements

S41003 . . . 0.030 1.50 0.040 0.010 1.00 10.5-12.5 1.50 . . . 0.030 . . .

Maximum, unless range or minimum is indicated.

Designation established in accordance with Practice E527 and SAE J 1086.

6. Heat Treatment

6.1 The material shall be heat-treated by tempering to meet

the requirements of this speciﬁcation. The tempering tempera-

ture shall not exceed 1400 °F [760 °C]. Prior to tempering, the

steel shall be in the as-rolled, normalized or quenched condi-

tion.

7. Mechanical Properties

7.1 The material shall conform to the mechanical properties

speciﬁed in Table 2.

8. Keywords

8.1 architectural steel; martensitic; plate; stainless steel;

steel; structural steel; tempered

SUPPLEMENTARY REQUIREMENTS

The following supplementary requirements shall apply only when speciﬁed individually by the

purchaser in the purchase order or contract. Requirements other than those shown in this section may

be speciﬁed subject to agreement between the supplier and the purchaser. The following supplemen-

tary requirements are suitable for use with this speciﬁcation.

S1. Charpy V-Notch Impact Test

S1.1 Charpy V-notch impact tests shall be conducted in

accordance with Speciﬁcation A673/A673M.

S1.2 The frequency of testing, the test temperature to be

used, and the absorbed energy requirements shall be as

speciﬁed on the order.

S2. Ultrasonic Examination

S2.1 The material shall be ultrasonically examined in ac-

cordance with the requirements speciﬁed on the order.

TABLE 2 Mechanical Test Requirements

Grade

Yield

Strength,

min, ksi

[MPa]

Tensile

Strength,

min, ksi

[MPa]

Elongation in

2 in. [50 mm],

min, %

Cold Blend

40 40 [275] 66 [455] 18 not required

50 50 [345] 70 [485] 18 not required

A1010/A1010M − 24

SUMMARY OF CHANGES

Committee A01 has identiﬁed the location of selected changes to this standard since the last issue

(A1010/A1010M – 13 (2018)) that may impact the use of this standard. (Approved March 1, 2024.)

(1) Added standardized text to subsections 1.4,1.5, and 1.6 to

the scope per Guide A994.

(2) Added reference to Terminology A941 and the titles of

referenced speciﬁcations.

(3) Added a terminology section and renumbered subsequent

sections.

ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentioned

in this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the risk

of infringement of such rights, are entirely their own responsibility.

This standard is subject to revision at any time by the responsible technical committee and must be reviewed every ﬁve years and

if not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standards

and should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of the

responsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you should

make your views known to the ASTM Committee on Standards, at the address shown below.

This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,

United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the above

address or at 610-832-9585 (phone), 610-832-9555 (fax), or service@astm.org (e-mail); or through the ASTM website

(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222

Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http://www.copyright.com/

A1010/A1010M − 24

文档加载中……请稍候！
如果长时间未打开，您也可以点击刷新试试。

下载文档到电脑，查找使用更方便

亲，本站95%以上的标准规范都面向会员免费，办理VIP会员下载更省钱，平均每篇不到2元

立即下载 VIP免费下载

已全部加载

标签： #马氏体不锈钢板 #薄板 #带

摘要：

ASTM A1010/A1010M-2024 Standard Specification for Higher-Strength Martensitic Stainless Steel Plate, Sheet , and Strip 更高强度马氏体不锈钢板,薄板和带的技术规范

展开>> 收起<<

ASTM A1010 - A 1010M - 24 更高强度马氏体不锈钢板,薄板和带的技术规范.pdf

共3页,预览3页

还剩页未读，继续阅读

声明：本文档系会员上传，若文档所含内容侵犯了您的版权或隐私，请立即通知，我们立即给予侵权申诉删除！

ASTM A1010 - A 1010M - 24 更高强度马氏体不锈钢板,薄板和带的技术规范

相关推荐

开通VIP享超值会员特权

相关内容

热门标签

举报选择: